Product Name: Ferrovanadium Nitride Powder

Ferrovanadium Nitride Powder Description: 

Ferrovanadium Nitride Powder Application:

1. FeVN alloy powder can be used for structural steel, tool steel, pipeline steel, steel, and cast iron.
2. It is used for nitrogen-containing steel melting: high- strength low-alloy steel (HSLA), rail steel, quick cutting steel, etc.

4. Ferrovanadium Nitride adding to the steel can increase the strength, tough, tactility, anti-thermal fatigue, etc.
5. It also can make the steel be able to fulfill solderability to attain the same strength, adding Ferrovanadium Nitride could save 30-40% of Vanadium, thereby saving the cost.

Ferrovanadium Nitride Powder Advantages:

1. Low melting point, high-density products, under the condition of the same production, vanadium and nitrogen yield is higher than similar products.
2. Low nitrogen vanadium than more reasonable, high strengthening ability.
3. Stable high product purity, ingredients, production has smaller fluctuation, the mechanical performance of steel performance has higher reliability.

Product Name: Iron Boride Powder

Iron Boride Powder Description

Iron Boride Powder is often used to improve abrasion resistance, corrosion resistance, wear resistance, and oxidation resistance. It is used in oil and gas refinery, chemical extraction, automotive agricultural, stamping, textile extrusion, and injection molding industries. Iron-based coatings recently gained attention for their mechanical, frictional, and corrosion-resistant properties. As compared to the ceramic or cermet type of materials people have used before, iron-based materials are relatively inexpensive, less strategic, and can be produced economically by various thermal methods with ease of fabrication and machining.

Iron Boride Powder Related Information

Niobium Boride Powder

Product Name: Niobium Boride Powder

Niobium Boride Powder

Niobium boride Powders having NbB, NbB2, and Nb3B4 phases in various amounts and single-phase NbB powders were successfully synthesized by using powder metallurgy methods from related metal oxide raw materials in the presence of a strong reducing agent. Nb2O5, B2O3, and Mg powder blends were milled at room temperature by a high-energy ball mill for a different time. Subsequently, an undesired MgO phase was removed from the milled powders by HCl leaching to constitute NbB–NbB2–Nb3B4 as final products, and they were subjected to an annealing process at 1500 °C for 4 h to observe probable boride transformation. Characterization was carried out by XRD, DSC, PSA, SEM/EDX, TEM, and VSM.

The effects of milling time (up to 9 h) on the formation, microstructure, and thermal behavior of the final products were investigated. The reduction reaction took place after milling stoichiometric powder blends for 2 h. Nano-sized NbB–NbB2–Nb3B4 powders in high purity were obtained in the absence of any secondary phase and any impurity via mechanochemistry by milling for 5 h and leaching with 4 mol/L HCl. After annealing, pure and nano-sized NbB–NbB2–Nb3B4 powders transformed to a single NbB phase without leaving behind NbB2 and Nb3B4 phases.

Vanadium Carbide Powder

Product Name: Vanadium Carbide Powder

Vanadium Carbide Description:

Application: 

1. Used in mechanical lapping
2. Used as engineering ceramic materials
3. Used for metallurgy refractory
4. Used for temperature hot accidentally
5. Used in faraday shield
6. Applies in flinty domains and so on thin film, target material, welding material, hard alloy, cermet, aerospace
7. May improve the hard alloy as the hard alloy and cermet’s chemical additive each performance.
8. It can be used in cutting tool and steel industry,
9. also can be used as an additive to fine the WC cemented carbide crystal to improve the property of alloy. 3. Used for erosion-resistant coatings; wear-resistance coatings; Corrosion-resistant coatings; Wear-resistant parts……

Vanadium Carbide Related Information