MXene Inks
MXene modified conductive flexible printed circuit with high conductivity and good adhesion
Product Code: NCZ-MX-228
Product |
Mxene Inks such as V2C Ink, Ti2C Ink, Ti3C2 Ink, Nb2C Ink |
Colour |
Black Powder/Ink |
Purity |
≥98 wt% |
Ingredient |
V2C, Ti2C, Ti3C2, Nb2C |
CAS NO |
12316-56-2 |
APPLICATION FIELDS
High-temperature coating, Mxene precursor, conductive self-lubricating ceramic, lithium-ion battery, supercapacitor, electrochemical catalysis.
Product features:
Good printability, electrical conductivity, high hardness, and strong adhesion. This kind of product has good bending resistance, low modulus, good performance, and excellent solvent resistance. Good adhesion to PET, PI, ITO substrate and FR substrate.
Typical applications: printing of electronic circuits such as membrane switches, keyboards, remote controls, flexible printed circuits, and FPCs. Miniature supercapacitor.
Instructions for use of Mxene Inks:
1. Applicable substrate: PET, PC, ITO, etc.
2. Stir: Stir thoroughly for 5 to 10 minutes before use.
3. Dilute: special diluent, the added proportion should not exceed 3% of the total weight.
4. Recommended process:
Printing thickness: wet film: 20μm; dry film: 4-7μm;
Silk screen: 250-300 mesh polyester or stainless steel screen printing;
Scraper: Polyurethane or solvent resistant material;
Equipment: Semi-automatic printing machine;
Curing conditions: Oven: 130 ℃ × 20 min IR furnace: 135 ℃ × 10 min (can be adjusted according to customer requirements)
Cleaning agent: acetone or diethylene glycol ether acetate.
Due to the significant environmental impact of the process, screen printing is recommended to be divided into batches and used up within 8 hours. Installing a protective cover can reduce the volatilization of product components and cut off dust particles in the air to ensure quality.
RELATED INFORMATION
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please email us for the customization.