Nickel Foil
₹0.00
Product: Nickel Foil (Ni, Purity: 99.9%, Thickness: 12 µm)
| Materials | Nickel Foil |
| Stock No. | NCZ-F-0015 |
| CAS | 7440-02-0 |
| Purity | ≥ 99.9% |
| Thickness | 12 μm, customization is available |
| Width | 30~500 mm, customization is available |
| Surface density | 8.908Â g/cm3 |
| Melting Point | 1455 °C |
| Boiling Point | 2730 °C |
| Joint | 1pcs/roll |
| Polished | One/Both Side Polished |
| Polished | One Side Coarse |
Description
Note: For pricing & ordering information, please contact us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities & Customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) are available upon request.
Shipping & Delivery
Related products
Aluminum Nanofoam
 Aluminum Metal Foams
| Product Name | Aluminum Foam |
| Stock No. | NCZFF114 |
| CAS | 7429-90-5 |
| Purity | 99.9% |
| Dimension | 100 mm×100 mm, customization is also possible |
| Thickness | 5 mm, customization is also possible |
| Pore size | 2-11 mm, customization is also possible |
| Molecular Formula | Al |
| Molecular Weight | 26.98 g/mol |
| Density | 0.1~0.35 g/cm³ |
| Porosity | 60-90%, customization is also possible |
| Compressive Strength | 44 Mpa |
| Bending Strength | 27 Mpa |
| Acoustic absorptive | 0.48 |
| Tensile Strength | 1.24 MPa |
| Shear Strength | 1.31 MPa |
| Modulus of Elasticity (Compression) | 103.08 MPa |
| Modulus of Elasticity (Tension) | 101.84 MPa |
| Shear Modulus | 199.95 MPa |
| Vickers Pyramid Number | 35 HV |
| Specific Heat | .895 J/g-C |
| Bulk Thermal Conductivity | 5.8 W/m-C |
| Bulk Resistivity | 2.84 × 10-5 ohm – in |
Aluminium Metal Foam Open Cell or Closed Cell in all size, PPI and thickness, Both are Available on demand (Ask for the customization)
Copper Foam
Product: Copper Foam Structures
Copper Foam Open Cell
Copper Metal Foams| Stock No. | NCZFF101 |
| PPI | 5-120, customization is also possible |
| Bulk Density | 0.80-0.85 g/cc |
| Purity | ≥ 99.9% |
| Porosity | ≥ 70%, customization is also possible |
| Dimension | 500mm X 500 mm, customization is also possible |
| Thickness | 1 to 25 mm, customization is also possible |
Physical Characteristics of heat-absorbing Copper Foam
| Compression Strength | 131 psi |
| Tensile Strength | 1000 psi |
| Shear Strength | 190 psi |
| Modulus of Elasticity (Compression) | 107 kpsi |
| Modulus of Elasticity (Tension) | 14.6 × 103 psi |
| Shear Modulus | 40.9 kpsi |
| Vickers Hardness | 35 |
| Specific Heat | 0.385 J/g-°C |
| Bulk Thermal Conductivity | 10.1 W/m-°C |
| Coefficient of Thermal Expansion | 1.7 × 10-5 m/m–°C (0-100°C) |
| Bulk Resistivity | 2.56× 10-5 ohm – in |
| Melting Point | 1080 °C |
Open Cell Copper Foam Heat Exchanger
Open Cell Copper Foam Heat Exchanger
Copper Metal Foam open cell
| Stock No. | NCZFF105 |
| PPI | 10 to 110 PPI, customization is also possible |
| Bulk Density | 0.80-0.85 g/cc |
| Purity | ≥99.9% |
| Porosity | ≥70%, customization is also possible |
| Dimension | 500 mm X 500 mm, customization is also possible |
| Thickness | 1 mm to 25 mm, customization is also possible |
| Compression Strength | 131 psi |
| Tensile Strength | 1000 psi |
| Shear Strength | 190 psi |
| Modulus of Elasticity (Compression) | 107 kpsi |
| Modulus of Elasticity (Tension) | 14.6 × 103 psi |
| Shear Modulus | 40.9 kpsi |
| Vickers Hardness | 35 |
| Specific Heat | 0.385 J/g-°C |
| Bulk Thermal Conductivity | 10.1 W/m-°C |
| Coefficient of Thermal Expansion | 1.7 × 10-5 m/m–°C (0-100°C) |
| Bulk Resistivity | 2.56× 10-5 ohm – in |
| Melting Point | 1080 °C |
Ask for customization while ordering
Polyethylene Foam
Product: Polyethylene Foam (Closed Cell, Purity: >99.9%)
CAS: 9002-88-4| Product Name | Polyethylene Foam |
| Product Code | NCZFF110 |
| Purity | >99.9% |
| Density | 1.2 (LB/Cubic Ft. |
| Color | White |
| Cell Count | 18 (cells/inch) |
COMPRESSIVE STRENGTH
| 25% | 7 (LB/In. Sq.) |
| 50% | 12 (LB/In. Sq.) |
COMPRESSION SET
| 2 hours | 30 % |
| 24 hours | 24 % |
| Compression Creep | 5 % |
| Water Absorption | 0.06 LB/Sq. Ft. |
| Thermal Stability | <2 % |
| Service Temperature | -30 to 180 °F |
| Contains Fire Retardant Additives | No |
Polyethylene Foam Closed Cell as well as Open Cell (Ask for customization while ordering)
Pure Silver Metal Sheet/Foil
Silver Foil Sheets (Ag foil, thickness 0.025 mm, ≥ 99.9% trace metals basis)
Silver Foil Sheets
Product: Silver Foil Sheets (Ag foil, thickness 0.025 mm, ≥ 99.9% trace metals basis)Â
Please send an email at sales@nanochemazone.com for the Size and Thickness customization.
| Materials | Silver Foil Sheets |
| Chemical Formula | Ag |
| Stock No. | NCZ-F-00117-R1 |
| CAS | 7440-22-4 |
| Purity | ≥ 99.9% |
| Thickness | 0.025 mm, 0.05 mm, 0.1 mm, 0.25 mm, 0.5 mm, 1 mm etc. (Customization is available on request) |
| Molecular Weight | 107.87 |
| EC Number | 231-131-3 |
| PubChem Substance ID | 24856080 |
| Density | 10.49 g/cm3(lit.) |
| Resistivity | 1.59 μΩ-cm, 20°C |
| Boiling Point | 2212 °C(lit.) |
| Melting Point | 960 °C(lit.) |
| Polished | Both Side Polished, one side polished, without Polish (Customization possible) |
| Appearance Quality | Foil/Sheet appearance |
| Size | 25 × 25 mm; 50 × 50 mm, 100 x 100 mm (Customization is available on request) |
Titanium Metal Foil
| Materials | Titanium Metal Foil |
| Stock No. | NCZ-F-0012 |
| CAS | 7440-32-6 |
| Purity | ≥ 99.9% |
| Thickness | 12 μm, customization is available on demand |
| Width | 30~500 mm, customization is available on demand |
| Surface density | 4.506Â g/cm3 |
| Melting Point | 1668 °C |
| Boiling Point | 3287 °C |
| Joint | 1pcs/roll |
| Polished | One/Both Side Polished |
| Polished | One Side Coarse |
Tungsten Metal Foil
Product: Tungsten Metal Foil (W, Purity: 99.9%, Thickness: 12 µm)
| Materials | Tungsten Metal Foil |
| Stock No. | NCZ-F-0014 |
| CAS | 7440-33-7 |
| Purity | ≥ 99.9% |
| Thickness | 12 μm / Customization is available |
| Width | 30~500 mm |
| Surface density | 19.25Â g/cm3 |
| Melting Point | 3422 °C |
| Boiling Point | 5930 °C |
| Joint | 1pcs/roll |
| Polished | One /Both Side Polished |
| Polished | One Side Coarse |