Product Name: Chromium Carbide Cr3C2 Powder

Product	Chromium Carbide
Colour	Gray Powder
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	Cr3C2
Product Code	NCZ-C-101/20
CAS Number	12012-35-0

Chromium Carbide Cr3C2 Powder APPLICATION FIELDS

Chromium Carbide Cr3C2 Powder is a ceramic compound that exists in several different chemical compositions: Cr3C2, Cr7C3, and Cr23C6. At standard conditions, it exists as a gray solid. It is extremely hard and corrosion-resistant. It is also a refractory compound, which means that it retains its strength at high temperatures as well. These properties make use as an additive to metal alloys. When chromium carbide crystals are integrated into the surface of a metal it improves the wear resistance and corrosion resistance of the metal and maintains these properties at elevated temperatures. Cr3C2 powder is mixed with solid nickel-chromium. This mixture is then heated to very high temperatures and sprayed onto the object being coated where it forms a protective layer. This layer is essentially its own metal matrix composite, consisting of hard ceramic Cr3C2 particles embedded in a nickel-chromium matrix. Cr3C2 prevents large grains from forming in the composite, which results in a fine-grained structure of superior toughness.

Chromium Carbide Cr3C2 Application:

1. Used as high temperature resistant and wear-resistant surface materials
2. Used for welding and flux-cored wire
3. Chromium carbide is useful in the surface treatment of metal components.
4. Chromium carbide is used to coat the surface of another metal in a technique known as thermal spraying.
5. Chromium carbide is used as an additive in cutting tools in order to improve toughness by preventing the growth of large grains.

Chromium Carbide Cr3C2 Properties:

There are three different crystal structures for chromium carbide corresponding to the three different chemical compositions. Cr₂₃C₆ has a cubic crystal structure and a Vickers hardness of 976 kg/mm². Cr₇C₃ has a hexagonal crystal structure and a microhardness of 1336 kg/mm². Cr₃C₂ is the most durable of the three compositions and has an orthorhombic crystal structure with a microhardness of 2280 kg/mm². For this reason, Cr₃C₂ is the primary form of chromium carbide used in surface treatment.   Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.  

Product Name: Ferrochrome Nitride Powder  

Product	Ferrochrome Nitride Powder
Colour	Black
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	FeCrN
Product Code	NCZ-CN-151/20
CAS Number	7439-89-6, / 24094-93-7

Ferrochrome Nitride Powder Description: Ferrochrome nitride is widely used in electric furnace and oxygen converter smelting nitrogen steel. Nitrogen is an element of austenite formation, It is used as a component to add chromium manganese and chromium manganese nickel stainless steel to replace the shortage of nickel. Ferrochrome Nitride Powder Application:

2. Widely used in stainless steel, heat resistant steel, corrosion-resistant steel, alloy steel, and other special steel smelting production
3. Used in steelmaking industrial, casting foundry

Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.                    

Niobium Boride Powder

Product Name: Niobium Boride Powder

MF	NbB
Chemical Name	Niobium Boride Powder
EINECS	235-723-2
Purity	99.9%
Molecular weight	103.72
Product Number	NCZ-SC-112/20
Cas Number	12007-29-3
Density	7.39g/ml

Niobium Boride Powder

Niobium boride Powders having NbB, NbB2, and Nb3B4 phases in various amounts and single-phase NbB powders were successfully synthesized by using powder metallurgy methods from related metal oxide raw materials in the presence of a strong reducing agent. Nb2O5, B2O3, and Mg powder blends were milled at room temperature by a high-energy ball mill for a different time. Subsequently, an undesired MgO phase was removed from the milled powders by HCl leaching to constitute NbB–NbB2–Nb3B4 as final products, and they were subjected to an annealing process at 1500 °C for 4 h to observe probable boride transformation. Characterization was carried out by XRD, DSC, PSA, SEM/EDX, TEM, and VSM.

The effects of milling time (up to 9 h) on the formation, microstructure, and thermal behavior of the final products were investigated. The reduction reaction took place after milling stoichiometric powder blends for 2 h. Nano-sized NbB–NbB2–Nb3B4 powders in high purity were obtained in the absence of any secondary phase and any impurity via mechanochemistry by milling for 5 h and leaching with 4 mol/L HCl. After annealing, pure and nano-sized NbB–NbB2–Nb3B4 powders transformed to a single NbB phase without leaving behind NbB2 and Nb3B4 phases.

RELATED INFORMATION Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.

Tungsten Carbide Powder

Product Name: Tungsten Carbide Powder

Product	Tungsten Carbide Powder
Colour	Grey
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	WC
Product Code	NCZ-C-109/20
CAS Number	12070-12-1

Brief Description of WC Tungsten Carbide Powder

Tungsten carbide powder (chemical formula: WC ) is a chemical compound (specifically, a carbide ) containing equal parts of tungsten and carbon atoms. In its most basic form, tungsten carbide is a fine Gray powder, but it can be pressed and formed into shapes for use in industrial machinery, cutting tools, abrasives, armor-piercing rounds, other tools and instruments, and jewelry. Physical Properties of WC Tungsten Carbide Powder Tungsten carbide has a high melting point at 2,870 °C (5,200 °F), a boiling point of 6,000 °C (10,830 °F) when under a pressure equivalent to 1 standard atmosphere (100 kPa), the thermal conductivity of 110 W·m−1·K−1, and a coefficient of thermal expansion of 5.5 µm·m−1·K−1. Tungsten carbide is extremely hard, ranking about 9 on Mohs scale, and with a Vickers number of around 2600. It has Young’s modulus of approximately 530–700 GPa, a bulk modulus of 630–655 GPa, and a shear modulus of 274 GPa. It has an ultimate tensile strength of 344 MPa, the ultimate compression strength of about 2.7 GPa and a Poisson’s ratio of 0.31. Chemical Properties of WC Tungsten Carbide Powder There are two well-characterized compounds of tungsten and carbon, WC and tungsten semi abide, W2C. Both compounds may be present in coatings and the proportions can depend on the coating method. At high temperatures, WC decomposes to tungsten and carbon and this can occur during high-temperature thermal spray, e.g., in high-velocity oxygen fuel (HVOF) and high energy plasma (HEP) methods.

Application of WC Tungsten Carbide Powder 

1 Used for Producing high capability nano-crystalline or superfine horniness alloy, hard-face abrasion-resistant spraying and petrochemical cracking catalyst;

2. Used for chipless forming tools; Cutting tools; Mining tolls; Nano-composites (for enhanced hardness, strength, and wear resistance);
3. Used for erosion-resistant coatings; wear-resistance coatings; Corrosion-resistant coatings; Wear-resistant parts
4. To produce hard carbide.

  Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.