Yttrium Aluminate Garnet |
| Cat No | NCZ-NSC817/20 |
| CAS No | 12253-70-2 |
| Purity | 99 % |
| APS | 30 nm (Can be customized) |
| Molecular Formula | Y3Al5O12 /Ce |
| Doping | Cerium – < 0.5% |
| Form | Powder |
| Color | Black |
| Density | 4.55 g/cm³ |
| Melting Point | 1970 °C |
| Hardness | 8.5Mohs |
| Thermal expansion | 0.8-0.9 x 10-5/K |
| Tensile Strength | 2 Gpa |
| Young’s modulus | 335 Gpa |
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Note: For pricing & ordering information, please contact us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities & Customization. E-mail: contact@nanochemazone.com
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) are available upon request.
You must be logged in to post a review.
Product |
Bentonite Clay Nanopowder |
| Cat No | NCZ-MN-113/20 |
| CAS No | 1302-78-9 |
| Purity | 99.9% |
| APS | < 80nm |
| Molecular Weight | 108.1 g/mol |
| Form | Powder |
| Specific Gravity | 2.5(H2O) |
| Melting Point | Decomposes |
| Solubility | Slightly soluble in water Insoluble in methanol |
| Molecular Formula | Al2H2O6Si |
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature. Â
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
| Product | Carbon Activated Powder |
| Cat No | NCZ-MN-158/20 |
| CAS No | 7440-44-0 |
| Purity | > 99.9% |
| APS | 25 mesh |
| Molecular Formula | C |
| Molecular Weight | 12.01g/mol |
| Form | Powder |
| Color | Black |
| Melting Point | 3550C (6422F) |
| Boiling Point | Sublimes |
| PH value | 5.0-10.0 |
| Specific Gravity | 250-600g/1 |
| % Volatiles by volume @ 21C (70F) | 0 |
| Vapor Density | 0.4 |
| Vapor pressure | 1 @ 3586C (6487F) |
| Solubility | Insoluble in water |
| Product | Gallium Arsenide Nanopowder |
| Cat No | NCZ-NSC810/20 |
| CAS No | 1303-00-0 |
| Purity | 99.9% |
| APS | 80-100nm |
| Molecular Formula | GaAs |
| Molecular Weight | 144.64g/mol |
| Form | Powder |
| Color | Gray |
| Density | 5.3g/cm3 |
| Melting Point | 1400°C |
| Young Modulus | 85 GPa |
| Thermal Conductivity | 47 W/m-K |
| Solubility in water | Insoluble in water |
Gallium Arsenide Nano powder composed of gallium arsenide nanoparticles (average particle size: 4?m) used in various semiconductor and photo optic applications. Gallium arsenide nano powder is hydrophobic and forms clear colloidal sultions in ethanol and non-polar solvents) Nanochemazone produces to many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available, as is additional technical and safety (MSDS) data. Please contact us for information on lead time and pricing above.
Storage Conditions:
Airtight sealed, avoid light, and keep dry at room temperature.Â
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
| Product | Lanthanum Hafnium Zirconate powder |
| Cat No | NCZ-MN-258/20 |
| CAS No | 12031-48-0 |
| APS | 1-10 µM, 10-25 µM 25- 45 µM (Customizable) |
| Purity | 99.5% |
| Form | White, odorless Powder |
| Density | 6.05 g/cm3 |
| Melting Point | ~ 2680 deg C |
| Solubility | Insoluble in Water |
| Formula | La2Zr2O7 |
| Hf | 2.2% |
| Fe | 0.01% |
| Na | 0.01% |
| Al | 0.1% |
| Si | 0.1% |
| Ca | 0.005% |
| Sr | 0.02% |
| Pb | 0.001% |
| Product | Palladium on Activated Charcoal Catalyst |
| Cat No | NCZ-MN-150/20 |
| CAS No | 7440-05-3 |
| Purity | >99.9% |
| APS | 40-60µm |
| Molecular Formula | Pd/C |
| Color | Black |
| Pd on Activated Charcoal | 1%, 2%, 3%, 4%, 5%, 10% |
| Surface Area, BET | ≥950 m²/g |
| Impurity | ≤0.3 % |
| Water Content | 0.1 % |
| Ash Content | ≤0.5 % |
| Product | Palladium on Alumina Catalyst |
| Cat No | NCZ-MN-151/20 |
| CAS No | 7440-05-3 |
| Purity | >99.9% |
| APS | 40-60µm |
| Molecular Formula | Pd/Al2O3 |
| Palladium on Alumina | 1%, 2%, 3%, 4%, 5%, 10% |
| Density | ≥0.55 g/ml |
| Surface Area, BET | ≥120 m²/g |
| Product | Tantalum Carbide Powder |
| Cat No | NCZ-MN-260/20 |
| CAS No | 12070-06-3 |
| APS | 1000 nm (customizable) |
| Purity | 99.9% |
| Molecular Formula | TaC |
| Molecular Weight | 192.96 g/mol |
| Form | Powder |
| Color | Gray |
| Density | 14.30 g/cm³ |
| Melting Point | 3,880 °C |
| Boiling Point | 4,780 °C |
| Solubility | Insoluble in water |
| Product | Carbonyl Iron Powder |
| Cat No | NCZ-MN-166/20 |
| CAS No | 7439-89-6 |
| Purity | 99.9% |
| APS | 5-10µm |
| Molecular Formula | Fe |
| Molecular Weight | 55.85g/mol |
| Form | Powder |
| Color | Gray |
| Density | 7.86g/cm3 |
| Melting Point | 1535°C |
| Boiling Point | 2750°C |
| Thermal Expansion | 11.8 µm•m-1•K-1 |
| Thermal Conductivity | 0.804 W/cm/K (298.2 K) |
| Vickers Hardness | 608 MPa |
| Poisson's Ratio | 0.29 |
| Electrical Resistivity | 9.71 µΩ•cm (20°C) |
| Electronegativity | 1.8 Paulings |
| Young's Modulus | 211 GPa |
| Specific Heat | 0.106 Cal/g/K @ 25°C |
| Heat of Fusion | 3.56 Cal/gm mol |
| Solubility | Insoluble in water |