Product Name: Ferro Titanium Carbide Powder

Product	Ferro Titanium Carbide Powder
Colour	Gray Powder
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	FeTiC
Product Code	NCZ-C-102/20
CAS Number	12604-56-7

Ferro Titanium Carbide Powder Applications Fields: Ferro Titanium Carbide Powder is a ferroalloy, an alloy of iron and titanium with between 10–20% iron and 45–75% titanium and sometimes a small amount of carbon. Ferrotitanium can be manufactured by mixing titanium sponge and scrap with iron and melting them together in an induction furnace. During steelmaking, titanium is usually introduced as ferrotitanium because of its relatively low melting temperature and high density. Ferrotitanium is usually produced by induction melting of titanium scrap with iron or steel; however, it also is produced directly from titanium mineral concentrates.

Application of Ferro Titanium carbide powder:

In the present study, Fe-based hardfacing coating reinforced by TiC particles was obtained by manual shielded metal arc welding (SMAW) in which H08A bare electrode was coated with fluxes, to which different measures of ferrotitanium, rutile, graphite, calcium carbonate, and calcium fluoride had been added.

The microstructure and wear properties of the hardfacing coating were studied through scanning electron microscopy (SEM), transmission electron microscopy (TEM), an X-ray diffractometer (XRD), and a wear test.

The results indicate that TiC particles are produced by a direct metallurgical reaction between ferrotitanium and graphite during welding.

TiC particles are uniformly dispersed in the matrix of lath martensite and retained austenite with particle sizes in the range of 3–5 μm. Fe-based hardfacing coating reinforced by TiC particles is found to possess better wear resistance and a lower coefficient of friction than that of the AISI 1045 steel substrate.

Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.    

Product Name: Ferrochrome Nitride Powder  

Product	Ferrochrome Nitride Powder
Colour	Black
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	FeCrN
Product Code	NCZ-CN-151/20
CAS Number	7439-89-6, / 24094-93-7

Ferrochrome Nitride Powder Description: Ferrochrome nitride is widely used in electric furnace and oxygen converter smelting nitrogen steel. Nitrogen is an element of austenite formation, It is used as a component to add chromium manganese and chromium manganese nickel stainless steel to replace the shortage of nickel. Ferrochrome Nitride Powder Application:

2. Widely used in stainless steel, heat resistant steel, corrosion-resistant steel, alloy steel, and other special steel smelting production
3. Used in steelmaking industrial, casting foundry

Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.                    

Niobium Boride Powder

Product Name: Niobium Boride Powder

MF:	NbB
Chemical Name	Niobium Boride Powder
EINECS:	235-723-2
Purity:	99.9%
Molecular weight:	103.72
Product Number:	NCZ-SC-112/20
Cas Number:	12619-90-8
Density	7.39g/ml

Niobium Boride Powder Related Information

Niobium boride powders having NbB, NbB2 and Nb3B4 phases in various amounts and single phase NbB powders were successfully synthesized by using powder metallurgy methods from related metal oxide raw materials in the presence of a strong reducing agent. Nb2O5, B2O3 and Mg powder blends were milled at room temperature

A high-energy ball mill for different time. Subsequently, an undesired MgO phase was removed from the milled powders by HCl leaching to constitute NbB–NbB2–Nb3B4 as final products, and they were subjected to an annealing process at 1500 °C for 4 h to observe probable boride transformation. Characterization was carried out by XRD, DSC, PSA, SEM/EDX, TEM, and VSM. The effects of milling time (up to 9 h) on the formation, microstructure, and thermal behavior of the final products were investigated.

The reduction reaction took place after milling stoichiometric powder blends for 2 h. Nano-sized NbB–NbB2–Nb3B4 powders in high purity were obtained in the absence of any secondary phase and any impurity via mechanochemistry by milling for 5 h and leaching with 4 mol/L HCl. After annealing, pure and nano-sized NbB–NbB2–Nb3B4 powders transformed into a single NbB phase without leaving behind NbB2 and Nb3B4 phases.

Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.    

Zirconium Carbide Powder

Product Name: Zirconium Carbide Powder

Product	Zirconium Carbide Powder
Colour	Black
Purity	≥ 99.9%
Particle size	1-10 µM (customizable)
Ingredient/MF	ZrC
Product Code	NCZ-C-110/20
CAS Number	12070-14-3

Zirconium Carbide Powder Description:

Like most carbides of refractory metals, zirconium carbide is sub-stoichiometric, i.e., it contains carbon vacancies. At carbon contents higher than approximately ZrC0.98 the material contains free carbon. ZrC reacts with water and acids and is pyrophoric. It becomes readily oxidized in the air when exposed to elevated temperatures. It shows a high amount of corrosion resistance property and contains carbon vacancies. It reacts with water as well as acids. Application: 1.Used as an abrasive, in metal cladding, in cermet, incandescent filaments, and cutting tools. 2. The mixture of zirconium carbide and tantalum carbide is an important cermet material. 3. Hafnium-free zirconium carbide and niobium carbide can be used as refractory coatings in nuclear reactors. 4. Zirconium carbide is used extensively as a coating of uranium dioxide and thorium dioxide particles of nuclear fuel. 5. The coating is usually deposited by thermal chemical vapor deposition in a fluidized bed reactor. 6.  High-temperature wear-resistant surface materials Please email us for the customization. Email: contact@nanochemazone.com Please contact us for customization and price inquiry Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.